Types

Gypsum plaster
Plaster of Paris is a type of building material based on calcium sulphate hemihydrate, nominally CaSO4·1/2H2O. It is created by heating gypsum to about 150 °C.[1]
2 CaSO4·2H2O → 2 CaSO4·0.5H2O + 3 H2O (released as steam).
A large gypsum deposit at Montmartre in Paris is the source of the name.[1][2] When the dry plaster powder is mixed with water, it re-forms into gypsum. Plaster is used as a building material similar to mortar or cement. Like those materials plaster starts as a dry powder that is mixed with water to form a paste which liberates heat and then hardens. Unlike mortar and cement, plaster remains quite soft after drying, and can be easily manipulated with metal tools or even sandpaper. These characteristics make plaster suitable for a finishing, rather than a load-bearing material.
One of the skills used in movie and theatrical sets is that of "plasterer", gypsum plaster often being used to simulate the appearance of surfaces of wood, stone, or metal. Nowadays, plasterers are just as likely to use expanded polystyrene, although the job title remains unchanged.
Lime plaster
Main article: Lime plaster
Lime plaster is a mixture of calcium hydroxide and sand (or other inert fillers). Carbon dioxide in the atmosphere causes the plaster to set by transforming the calcium hydroxide into calcium carbonate (limestone). Whitewash is based on the same chemistry.
To make lime plaster, limestone (calcium carbonate) is heated to produce quicklime (calcium oxide). Water is then added to produce slaked lime (calcium hydroxide), which is sold as a white powder. Additional water is added to form a paste prior to use. The paste may be stored in air-tight containers. Once exposed to the atmosphere, the calcium hydroxide turns back into limestone, causing the plaster to set.
Lime plaster was a common building material for wall surfaces in a process known as lath and plaster, whereby a series of wooden strips on a studwork frame was covered with a semi-dry plaster that hardened into a surface. The plaster used in most lath and plaster construction was mainly lime plaster, with a cure time of about a month. To stabilize the lime plaster during curing, small amounts of Plaster of Paris were incorporated into the mix. Because Plaster of Paris sets quickly, "retardants" were used to slow setting time enough to allow workers to mix large working quantities of lime putty plaster. A modern form of this method uses expanded metal mesh over wood or metal structures, which allows a great freedom of design as it is adaptable to both simple and compound curves. Today this building method has been partly replaced with drywall, also composed mostly of gypsum plaster. In both these methods a primary advantage of the material is that it is resistant to a fire within a room and so can assist in reducing or eliminating structural damage or destruction provided the fire is promptly extinguished.
Lime plaster is used for true frescoes. Pigments, diluted in water, are applied to the still wet plaster.
Cement plaster
See also: Cement render
Cement plaster is a mixture of suitable plaster, sand, portland cement and water which is normally applied to masonry interiors and exteriors to achieve a smooth surface. Interior surfaces sometimes receive a final layer of gypsum plaster. Walls constructed with stock bricks are normally plastered while face brick walls are not plastered. Various cement-based plasters are also used as proprietary spray fireproofing products. These usually use vermiculite as lightweight aggregate. Heavy versions of such plasters are also in use for exterior fireproofing, to protect LPG vessels, pipe bridges and vessel skirts.